Hi-Pon 50-01 Polyurethane 5 Litre

PRODUCT DESCRIPTION

Hi-Pon 50-01 Polyurethane Top Coat is a two-pack, aliphatic acrylic polyurethane finish coat. It provides high durability, excellent gloss and colour retention. It also offers good abrasion, chemical and impact resistance when applied over proven systems.

INTENDED USE

It is designed for use in both new construction and as an industrial maintenance finish which can be used in a wide range of environments including offshore structures, refineries, power plants, bridges, transportation vehicles and buildings.

GENERAL PROPERTIES

Colour : Standard colours as per colour cards Special colours available upon request

Gloss Level : High-Gloss

Volume Solid : 60 ± 2 %

Specific Gravity : 1.12 ± 0.10 kg/l (Mixed) – depending on colours

Flash Point : Base: 23 °C Hardener: 23 °C Mix: 23 °C

VOC : 386 g/L (EPA Method 24)

Typical Thickness : 50 – 80 µm dry film 83 – 133 µm wet film

SURFACE PREPARATION

All surfaces should be clean dry, and free from contamination. The surface should be assessed and treated in accordance with ISO 8504. Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning. Damaged Area Damage area should be prepared with abrasive blast cleaning to Sa 2½ (ISO 8501-1) or SSPC-SP10. When abrasive blasting is not possible, mechanical cleaning to St3 (ISO 8501-1) or SSPC-SP3 is acceptable. After the surface preparation, patch suitable primer prior to the application of Hi-Pon 50-01. Other Surfaces The coating may be used on other substrates. Please contact your local Nippon Paint office for more information.

CONDITION DURING APPLICATION

Avoid paint application when the temperature is below 10 °C and relative humidity is above 85 %. The temperature of steel surface must be minimum 3 °C above dew point of surrounding air.

APPLICATION GUIDE

Mixing Ratio : BASE : 4 , HARDENER  : 1 (by volume)